    Kinetic and chemorheological modeling of thermosetting polyurethanes obtained from an epoxidized soybean oil polyol crosslinked with glycerin
    (2022-10) Armanasco, Franco; Chiacchiarelli, Leonel Matías; D'hers, Sebastián
    "Thermosetting polyurethanes were obtained using an aromatic isocyanate and a hydrophobic polyol formulation obtained from epoxidized soybean oil (ESO) crosslinked with glycerin. A systematic DSC analysis of the effect of catalyst type, crosslinker concentration, isocyanate index and ESO crystallization on cure kinetics was conducted. The combination of a stannic catalyst at 0.2 wt% and glycerin at 20 wt% produced a cure kinetics governed by an autocatalytic heat flow where vitrification played a key role in the formation of chemical bonds. The evolution of Tg as a function of conversion, which followed Di-Benedetto's predictions, supported the hypothesis that vitrification was a preponderant phenomenon during cure. Dynamic Mechanical Analysis (DMA) of a post-cured sample revealed a Tg centered at 220°C, whereas quasi-static flexural mechanical tests shown a flexural modulus of 2.14 GPa and a flexural strength of 99.4 MPa. Rheological experiments at isothermal conditions supported the hypothesis that vitrification played a key role in the evolution of apparent viscosity. A master model using Kim-Macosko equations was obtained for the proposed formulation. The results presented in this work will serve to further extend the use of biobased polymers applied in the polymer composite industry."
  • Thumbnail Image
    artículo de publicación periódica.listelement.badge
    Nanostructured rigid polyurethane foams with improved specific thermo-mechanical properties using bacterial nanocellulose as a hard Segment
    (2021-01) Chiacchiarelli, Leonel Matías; Benavides, Sara; Armanasco, Franco; Cerrutti, Patricia
    "Bacterial nanocellulose (BNC) was used to synthesize rigid polyurethane foams (RPUFs) based on its reaction with the isocyanate precursor (ISO route) and also by using the conventional procedure (POL route). The results indicated that at only 0.1 wt. % of BNC, drastic improvements of specific elastic compressive modulus (+244.2 %) and strength (+77.5 %) were found. The reaction of BNC with the precursor was corroborated through the measurement of isocyanate number and the BNC caused a significant nucleation effect, decreasing the cell size up to 39.7%. DSC analysis revealed that the BNC had a strong effect on post-cure enthalpy, decreasing its value when the ISO route was implemented. DMA analysis revealed that the RPUFs developed using the ISO route proved to have an improved damping factor, regardless of BNC concentration. These results emphasize the importance of using the ISO route to achieve foamed nanocomposites with improved specific mechanical properties."